Kimyasal Bileşimi
JIS Özellikler
ASTM Şartname
şartname |
Çelik Sınıf |
% C Maks. |
Si% Maks. |
% Mn Maks. |
P% Maks. |
S% Maks. |
Cr% | % Ni | % Mo | Ti% | DİĞER |
JIS G4303 G4304 G4305 G4312 |
SUS301 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 16.00-18.00 | 6,00-8,00 | |||
SUS302 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 8,00-10,00 | ||||
SUS304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 18.00-20.00 | 8,00-10,50 | ||||
SUS304L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 18.00-20.00 | 9.00-13.00 | ||||
SUS304J3 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 8,00-10,50 | Cu: 1,00-3,00 | |||
SUH309 | 0.20 | 1.00 | 2.00 | 0.045 | 0.03 | 22,00-24,00 | 12,00-15,00 | ||||
SUS309S | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 22,00-24,00 | 12,00-15,00 | ||||
SUH310 | 0.25 | 1.50 | 2.00 | 0.045 | 0.03 | 24,00-26,00 | 19,00-22,00 | ||||
SUS310S | 0.08 | 1.50 | 2.00 | 0.045 | 0.03 | 24,00-26,00 | 19,00-22,00 | ||||
SUS316 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 16.00-18.00 | 10,00-14,00 | 2,00-3,00 | |||
SUS316L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 16.00-18.00 | 12,00-15,00 | 2,00-3,00 | |||
SUS317 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 18.00-20.00 | 11,00-15,00 | 3,00-4,00 | |||
SUS321 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 9.00-13.00 | 5 * C Min. | |||
SUS347 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 9.00-13.00 | Nb: 10 * C Min. | |||
SUSXM7 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 8,50-10,50 | Cu: 3,00-4,00 | |||
SUH409 | 0.08 | 1.00 | 1.00 | 0.040 | 0.03 | 10,50-11,75 | 0,75 ila 6 ° C | ||||
SUH409L | 0.03 | 1.00 | 1.00 | 0.040 | 0.03 | 10,50-11,75 | 0,75 ila 6 ° C | ||||
SUS410 | 0.15 | 1.00 | 1.00 | 0.040 | 0.03 | 11,50-13,50 | |||||
SUS420J1 | 0,16-0,25 | 1.00 | 1.00 | 0.040 | 0.03 | 12,00-14,00 | |||||
SUS420J2 | 0,26-0,40 | 1.00 | 1.00 | 0.040 | 0.03 | 12,00-14,00 | |||||
SUS430 | 0.12 | 0.75 | 1.00 | 0.040 | 0.03 | 16.00-18.00 | |||||
SUS434 | 0.12 | 1.00 | 1.00 | 0.040 | 0.03 | 16.00-18.00 | 0.75 ~ 1.25 |
ASTM Şartname
şartname | Çelik Sınıf | % C Maks. |
Si% Maks. |
% Mn Maks. |
P% Maks. |
S% maksimum |
Cr% | % Ni | % Mo | Ti% | DİĞER |
ASTM A240 |
S30100 | 0.15 | 1.0 | 2.00 | 0.045 | 0.03 | 16.00-18.00 | 6,00-8,00 | N: 0.10 Max | ||
S30200 | 0.15 | 0.75 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 8,00-10,00 | N: 0.10 Max | |||
S30400 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 18.00-20.00 | 8,00-10,5 | N: 0.10 Max | |||
S30403 | 0.03 | 0.75 | 2.00 | 0.045 | 0.03 | 18.00-20.00 | 8,00-12,00 | N: 0.10 Max | |||
S30908 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 22,00-24,00 | 12,00-15,00 | ||||
S31008 | 0.08 | 1.50 | 2.00 | 0.045 | 0.03 | 24,00-26,00 | 19,00-22,00 | ||||
S31600 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 16.00-18.00 | 10,00-14,00 | 2,00-3,00 | N: 0.10 Max | ||
S31603 | 0.03 | 0.75 | 2.00 | 0.045 | 0.03 | 16.00-18.00 | 10,00-14,00 | 2,00-3,00 | N: 0.10 Max | ||
S31700 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 18.00-20.00 | 11,00-15,00 | 3,00-4,00 | N: 0.10 Max | ||
S32100 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 9.00-12.00 | 5 * (C + N) Min. 0,70 Max |
N: 0.10 Max | ||
S34700 | 0.08 | 0.75 | 2.00 | 0.045 | 0.03 | 17.00-19.00 | 9.00-13.00 | Cb: 10 * CM. 1.00 Max |
|||
S40910 | 0.03 | 1.00 | 1.00 | 0.045 | 0.03 | 10,50-11,70 | 0.5Max | Ti: 6 * Cmin. 0.5 Maks. |
|||
S41000 | 0.15 | 1.00 | 1.00 | 0.040 | 0.03 | 11,50-13,50 | 0.75Max | ||||
S43000 | 0.12 | 1.00 | 1.00 | 0.040 | 0.03 | 16.00-18.00 | 0.75Max |